Thermal Furnace Mullite Refractory Bricks , High Heat Cement Kiln Fire Bricks

Categories Mullite Refractory Bricks
Brand Name: Jansincere
Model Number: MRB-021
Certification: ISO9001:2015
Place of Origin: Xinmi City, Henan, China
MOQ: 5 tons
Price: US$418.00-US$ 645 per ton of silicon mullite bricks and negotiable
Payment Terms: L/C, T/T, Western Union
Supply Ability: 45000 ton of silicon mullite bricks per year
Delivery Time: 30-45 days
Packaging Details: Wooden pallet, plastic shrink film, paper corner protection and straps protected outside. Pallet size: 95*95cm, 100*100cm or as request.
Product Name: Silica Mullite Refractory Brick
Al2O3 Content: ≥60%
Bulk Density: ≥2.55 g/cm³
Apparent Porosity: ≤19%
Cold Crushing Strength: ≥90 Mpa
RUL T0.6: ≥1550℃
Thermal Shock Resistance: ≥12 times (1100℃, water cooling)
Raw Material: High alumina content bauxite
Application: Rotary kiln
Size: Standard Size
Refractoriness: 1550-1700 ℃
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    Thermal Furnace Mullite Refractory Bricks , High Heat Cement Kiln Fire Bricks


    Cement Kiln Fire Bricks Thermal Refractory Furnace Mullite Brick


    Introduction:

    Silicon mullite abrasion resistant brick is made of special grade high bauxite clinker and silicon carbide as the main raw material pressed in high pressure and sintered in high temperature, having the cold crushing strength, high structure strength at high temperature, good thermal shock resistance, constantly forming the protection layer in use, good wear-resistance, strong anti-exfoliation, used for the part of transition band, cooling zone and kiln eye etc. in cement kiln.


    Technical Index:

    ItemSilicon Mullite Bricks
    GM1650GM1600GM1550
    Chemical ComponentAl2O3/% ≥656360
    Physical PropertiesBulk Density g/cm32.622.602.55
    Apparent Porosity % ≤171719
    Crushing Strength MPa ≥859090
    Refractoriness Under Load T0.6/℃ ≥165016001550

    Thermal Shock Resistance

    (1100℃~water cooling) times ≥

    101012
    Cold Crushing Strength cm35
    * Thermal Expansion Rate/%Offer actual measurement data

    Above parameters is guarantee value. Specification can be customized as actual working condition.


    Achievements:

    We have supplied high strength alkali resistance brick, anti-spalling high alumina brick, silicon mullite brick and mortar for Jiande Hongshi Cement Co., Ltd.


    FAQ:

    1. When Jansincere Company established?

    In 1986.

    2. How many staffs in your factory?

    About 500, including including 23 managers, 42 technicians, and 8 qualified installation engineers.

    3. What’s your main products scope?

    Our main products are dense refractory bricks and monolithic refractories, including alumino-silicate refractories, magnetite-alumina refractory, special high grade refractories, refractory cement, castable refractory and so on.


    Our Company:

    Zhengzhou Jansincere Refractory Co., Ltd was founded in 1986.

    Jansincere Refractory is focused on providing professional refractory design, manufacturing, installation and kiln maintenance for aluminum, non-ferrous metallurgy, cement, environment and energy solutions, and petroleum industries.

    Quality Thermal Furnace Mullite Refractory Bricks , High Heat Cement Kiln Fire Bricks for sale
    Send your message to this supplier
     
    *From:
    *To: Zhengzhou Jansincere Refractory Co., Ltd
    *Subject:
    *Message:
    Characters Remaining: (0/3000)
     
    Inquiry Cart 0

    Friendly Links: www.everychina.com

    Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

    Copyright © 2009 - 2024 xpshou.com. All rights reserved.